Reliable PA 6 Chips Granules for Durable Engineering and Electrical Solutions

Product Description

Product Description

1.Product Description

Polyamide-6 is an aliphatic polyamide, with light weight, high strength, wear resistance, resistance to weak acid and weak alkali
and some organic solvents, easy molding and processing and other excellent properties, widely used in fiber, engineering plastics
and films and other fields.

2. PA6 product features:

High mechanical strength, good toughness, high tensile and compressive strength,Outstanding fatigue resistance,
High softening point, heat resistant,
wear-resistant,Corrosion resistance,
It has self-quenching, good weather resistance, good antibacterial and mildew resistance,
Good electrical insulation,
Low melting viscosity, fast flow, easy to fill mold,etc

Properties	Test Method	Test Condition	Unit	Typical Values(dry)
Physical properties
Specific Gravity	ISO 1183	23°C	g/cm³	1.71
Ash	ISO 3451	800°C,30min	%	60
Mechanical properties
Tensile Strength	ISO 527	5mm/min	MPa	235
Tensile Modulus	ISO 527	1mm/min	MPa	22000
Elongation at Break	ISO 527	5mm/min	%	2.2
Flexural Strength	ISO 178	2mm/min	MPa	400
Flexural Modulus	ISO 178	2mm/min	MPa	20000
Unotched Charpy Impact Strength	ISO 179-1/1eU	23°C	kJ/m2	95
Notched Charpy Impact Strength	ISO 179-1/1eA	23°C	kJ/m2	18
Thermal properties
Heat deflection temperature	ISO 75	1.80MPa	°C	212
Melt Temperature	ISO 11357	DSC	°C	220
Other properties
Mold Shrinkage	internal test method	flow direction	%	TBD
		cross flow direction	%	TBD
Flammability	ISO 3795	-	mm/min	30

 

Processing Conditions		Range
Melt Temperature		240-270°C
Barrel Temperature	Rear	240--250°C
	Center	250--260°C
	Front	260--270°C
Mold Temperature		70-100°C
Pre-Dry needed		110-120°C, 4-6h  dehumidified dryer
Note: The above process condition is only for reference. The actual process should be adjusted according to different type of machine, mold design and product design.

Packaging Details
It is packed with polythene bag as the inner layer, and polywoven bag as the outer layer. The net weight of each bag is 25kg.
Port
QINGDAO
Lead Time:

Quantity(tons)	1 - 100	>100
Est. Time(days)	7	To be negotiated

FAQ